پژوهشگاه رنگ با همکاری انجمن علمی رنگ ایرانعلوم و فناوری رنگ1735-87798320140923Study the Effect of Substitution of Zirconium Silicate in the Ceramic Glaze by Aluminum Silicate, MgO, CaO and Al2O3 on the Optical Propertiesبررسی اثر جایگزینی سیلیکات زیرکونیم با سیلیکات آلومینیم و اکسیدهای کلسیم، منیزیم و آلومینیم در لعابهای سرامیکی بر خواص نوری سطح سرامیک17918676126FAفرزانهکرم پوررادگروه نانوفیزیک و مغناطیس، دانشگاه یزدمحسنخواجه امینیاندانشکده فیزیک ، آزمایشگاه نانوفیزیک و مغناطیس، دانشگاه یزد0000-0003-2396-8092محسنحکیمیگروه نانوفیزیک و مغناطیس، دانشگاه یزدJournal Article19700101To make a white surface of ceramic glazes, zirconium silicate (zircon) particles are dispersed in the glaze body. Due to the high difference between the refractive index of zircon particles and that of the glazed body, the surface of the glaze scatters and reflects most of the light. Since zircon is expensive, some research has been done to find a cost-effective alternative for it. In this paper zircon was substituted by CaO, MgO, Al2O3 and also aluminum silicate as frit in the ceramic glaze and the effects on the physical properties of the surface were studied. Some samples with these materials were prepared and the reflectance spectra, whiteness index and the color parameters in CIEL*a*b* color space were studied. To study the composition and microstructure of the samples SEM and XRD experiments were performed. The results shown the sample which some part of zircon in the opacifier layer (engobe) was substituted by new compounds, had almost the same properties as full zircon sample.برای ایجاد سفیدی سطح لعابهای سرامیکی ماده سیلیکات زیرکونیم (زیرکن) بصورت ذرات مجزایی در لعاب پخش میشود که با توجه به اختلاف زیاد ضریب شکست این ماده با ضریب شکست بدنه لعاب مقداری از نور تابیده را پراکنده و بازتاب میکند. قیمت بالای زیرکن باعث پژوهشهایی برای جایگزینی آن با مواد ارزانتر شده است. در این تحقیق تاثیر جایگزینی اکسیدهای منیزیم، کلسیم، آلومینیم و نیز سیلیکات آلومینیم بجای زیرکن در لعاب سرامیک بر خواص فیزیکی سطح مورد بررسی قرار گرفته است. برای بررسی تاثیر استفاده از این مواد بر ظاهر رنگی لعاب کاشی، طیف بازتاب نوری، شاخص سفیدی و پارامترهای رنگی در فضا رنگ CIEL*a*b* نمونههای مختلف اندازهگیری و با یکدیگر مقایسه شدند. همچنین برای مطالعه ساختار بلوری و ریزساختار سطح آزمایشهای پراش پرتو X و میکروسکوپ الکترونی بر روی نمونهها انجام شدند. نتایج نشان میدهد جانشینکردن بخشی از زیرکن با ترکیبات یاد شده در لایه پشتپوشکننده (انگوب)، شاخص سفیدی تقریبا برابر با نمونه مرجع (زیرکن کامل) را نتیجه میدهد. طیف بازتاب و جذب آب نیز نزدیک بودن نمونه جایگزین و نمونه مرجع را تایید میکند.پژوهشگاه رنگ با همکاری انجمن علمی رنگ ایرانعلوم و فناوری رنگ1735-87798320140923Investigating the Performance of NIR Spectrometry for Identifying Madder as a Natural Dye from Synthetic Dyes Used in Handmade Carpetبررسی کارایی روش طیفسنجی زیرقرمز نزدیک در شناسایی رنگزای طبیعی روناس از رنگزای مصنوعی، مورد استفاده در خامه فرش دستباف18719276127FAسعیدهگرجی کندیدانشکده مهندسی پلیمر و رنگ، دانشگاه صنعتی امیرکبیرکمالالدینقرنجیگگروه پژوهشی مواد رنگزای آلی، قطب علمی رنگ، موسسه پژوهشی علوم و فناوری رنگ و پوشش0000-0002-0115-3557Journal Article19700101Due to the difference between price and value of natural versus synthetic dyes, it has always been very important to distinguish these two categories for handmade carpet. This study aimed to investigate Near-IR spectrometry technique to identify natural madder and synthetic dyes used in handmade carpets. To do this woolen samples with two major races (Baluchi and Kermanshahi) were dyed with madder dye with alum and tin chloride mordant, and also synthetic dyes to provide conventional red-colored shades. The 60 dyed samples including of 24 madder, a set of 10 mixed (combination of Madder and synthetic dyes), 26 synthetic dyes, and 5 cases gotten from carpet, and in total 65 samples were prepared. Results showed that the spectral reflectance of the madder samples has an increasing slope in NIR region while the NIR spectral reflectance of synthetic dyes does not show any noticeable increasing trend. Considering the obtained results of this research, NIR spectrometry can be a feasible method to distingush between madder and synthetic dyes and it was quiet possible for the test samples with almost no errors. However, investigating on more samples would be suggested. Note that it is not possible to detect samples dyed with a mixture of madder and synthetic dyes. The mixed samples were presented in one of the two groups; synthetic or madder.با توجه به تفاوت قیمت و ارزش رنگزاهای طبیعی در مقابل مصنوعی، شناسایی این دو دسته در فرش دستباف از اهمیت بسیاری برخوردار است. در این تحقیق هدف بررسی روش طیفسنجی زیر قرمز نزدیک جهت شناسایی رنگزای طبیعی روناس از رنگزاهای مصنوعی مورد استفاده در فرش دستباف میباشد. برای انجام این مهم نمونههای نخ پشمی با دو نژاد بلوچی و کرمانشاهی با رنگزای طبیعی روناس با دندانههای زاج سفید و کلرید قلع و رنگزاهای مصنوعی جهت تهیه فامهای رنگی متداول قرمز رنگرزی گردید. بدین ترتیب 60 نمونه رنگرزی شده شامل 24 نمونه روناس، 10 نمونه ترکیبی، 26 نمونه مصنوعی، و 5 نمونه از صنعت، و در مجموع 65 نمونه تهیه شد. نتایج نشان میدهد طیف انعکاسی نمونههای رنگرزی شده با روناس در ناحیه NIR همچنان شیب افزایشی دارد درحالی که برای نمونههای رنگرزی شده با رنگزاهای مصنوعی افزایش چندانی را نشان نمیدهد. با توجه به نتایج این طرح، شناسایی روناس از نمونههای مصنوعی با بررسی طیف NIR نمونهها کاملا امکانپذیر بود و برای نمونههای مورد بررسی تقریبا بدون هیچ خطایی شناسایی انجام شد. هرچند بررسی بر روی تعداد نمونههای بیشتر پیشنهاد میشود. البته در مورد نمونههایی که با مخلوط روناس و رنگزای مصنوعی رنگرزی شده بودند شناسایی امکانپذیر نشد. این نمونهها جزء یکی از دو گروه مصنوعی یا طبیعی قرار می گرفتند.پژوهشگاه رنگ با همکاری انجمن علمی رنگ ایرانعلوم و فناوری رنگ1735-87798320140923Dye Removal From Reactive Dye Wastewater Using β–cyclodextrin Functionalized Polyacrylonitrile Nanofibersرنگبری پساب رنگزای راکتیو توسط نانوالیاف پلیاکریلونیتریل عاملدار شده با بتاسیکلودکسترین19320176128FAصدیقهبرهانیدانشکده مهندسی نساجی، دانشگاه صنعتی اصفهانهالهخلیلیدانشکده مهندسی نساجی، دانشگاه صنعتی اصفهاننسیمسوهانکاردانشکده مهندسی نساجی، دانشگاه صنعتی اصفهانفوزیفروزمهردانشکده مهندسی نساجی، دانشگاه صنعتی اصفهانJournal Article19700101The main aim of this study is investigation of the reactive dye removal efficiency from wastewater by using nanofibers functionalized with β-cyclodextrin(βCD) through the immersion method. At first, polyacrylonitrile(PAN) nanofibers for the removal of three reactive dyes of CI Reactive Blue 13, C.I. Reactive Blue 21 and C.I. Reactive Red 2 from simulated wastewater were used. The dye removal efficiency for the dyes mentioned was 4.7, 22.5 and 3.4 %, respectively. Then, PAN/βCD10 and PAN/βCD50 nanofibers, which had 10 and 50 wt% of βCD, respectively, were electrospun. It was found that dye removal efficiency of PAN/βCD10 nanofiber mats for the dyes mentioned was 8.3, 28.1and 10 %, respectively. Also, dye removal efficiency of PAN/βCD50 nanofiber mats was obtained to be 31, 49 and 25%. Based on the results, dye removal efficiency of reactive dye wastewater was increased due to the increase in βCD concentration. Increasing PAN/βCD50 nanofibers weight from 0.01 to 0.1 g tended to increase dye removal efficiency of C.I Reactive Blue 21 dye wastewater from 49% to 86.4%.هدف این تحقیق ارزیابی بازده رنگبری نانوالیاف عاملدار شده با سیکلودکسترین (βCD) جهت حذف رنگزای راکتیو از پساب، به روش غوطهوری است. نانوالیاف پلیاکریلونیتریل(PAN) برای حذف رنگزاهای راکتیو C.I. Reactive Blue 13، C.I. Reactive Blue 21 و C.I. Reactive Red 2 از پساب رنگرزی استفاده و بازده رنگبری برای رنگزاهای فوق به ترتیب 4.7%، 22.5% و 3.4% حاصل شد. سپس نانوالیاف PAN/βCD10 و PAN/βCD50 به ترتیب حاوی 10 و 50 درصد وزنی بتاسیکلودکسترین، تهیه شد. بازده رنگبری نمونه PAN/βCD10 به ترتیب 8.3%، 28.1% و 10% و برای نمونه PAN/βCD50 به ترتیب 31%، 49% و 25% بهدست آمد. حضور و افزایش میزان سیکلودکسترین منجر به افزایش بازده رنگبری شد. افزایش وزن نانوالیاف PAN/βCD50 در پساب رنگزای C.I Reactive Blue 21 از 0.01 به 0.1 گرم، با افزایش بازده رنگبری از 49% به 86.4% همراه بود. بر اساس نتایج حاصل میتوان نانوالیاف PAN/βCD را انتخاب مناسبی جهت حذف رنگزای راکتیو از پساب رنگرزی معرفی کرد.پژوهشگاه رنگ با همکاری انجمن علمی رنگ ایرانعلوم و فناوری رنگ1735-87798320140923Photocatalytic Degradation of Dye Using Dopping Titanium Dioxide Nanoparticles and its Kinetic Studyحذف فوتوکاتالیزی رنگزا با استفاده از نانوذرات دی اکسید تیتانیم تلقیح شده و مطالعه سینتیکی آن20321176129FAزهرامینائی زنگیگروه مهندسی محیطزیست، دانشگاه تربیت مدرسحسینگنجی دوستگروه مهندسی محیطزیست، دانشگاه تربیت مدرسبیتاآیتیگروه مهندسی محیطزیست، دانشگاه تربیت مدرس0000-0001-7720-9863Journal Article19700101Dyes are one of the wastewater pollutants that use of them is increasing every day. In this study, the dye degradation efficiency with Zn-TiO2 was investigated using the sun as a light source. The effect of zinc on dopant activity and kinetics of dye degradation from wastewater was also investigated. Dopant was made with synthesis induction- evaporation method. The experiments were performed in a continuously photo reactor throughout the day. According to the results, at pH of 6.9, 50 mg /L of dye concentration, 50 mg/m2 catalyst concentration and Zn /Ti equal to 53% within 5 h; dye removal and organic degradation efficiency were obtained 85 and 60 %, respectively. According to the results, the reaction kinetics was pseudo-first-order equation.رنگزاها یکی از منابع آلایندگی پساب ها هستند که مصرف آنها روز به روز در حال افزایش است. در این تحقیق، کارایی ترکیب تلقیحی (Dopant) Zn-TiO2 در حذف رنگزای سه آزوئی DB71 با استفاده از خورشید به عنوان منبع نور، اثر مقدار فلز روی تلقیح شده و سینتیک حذف رنگزا از پساب بررسی شد. ترکیب تلقیحی مورد بررسی به روش سنتز القایی- تبخیری ساخته و آزمایشات در یک فوتوراکتور خورشیدی پیوسته در طول روز انجام شد. در این تحقیق پارامترهای نسبت Zn/Ti، غلظت رنگزا، غلظت فوتوکاتالیست، pH و شدت تابش نور خورشید بررسی شد. طبق نتایج حاصل در pH برابر با 6.9، غلظت کاتالیست 50 گرم بر متر مربع با نسبت Zn/Ti برابر با %0.53، غلظت 50 میلیگرم بر لیتر رنگزا در مدت زمان 5 ساعت، 85 درصد رنگزا و 60 درصد COD حذف شد. همچنین سینتیک حذف رنگ تطبیق خوبی با مدل شبه مرتبه اول نشان داد.پژوهشگاه رنگ با همکاری انجمن علمی رنگ ایرانعلوم و فناوری رنگ1735-87798320140923Synthesis and Characterization of UV-Curable Carboxylated Urethane Acrylate as an Anionic Polymeric Dispersant and Dispersion Study of SiO2 and TiO2سنتز و شناسایی یورتان آکریلات تابشپز با گروههای کربوکسیل به عنوان پراکنشگر آنیونی پلیمری و بررسی پراکنش سیلیکا (SiO2) و دیاکسید تیتانیم (TiO2)21322076130FAفاطمهمهرعلیگروه شیمی آلی، دانشگاه پیام نور تهرانفرهودنجفیگروه رزین و افزودنیها، پژوهشکده پوششهای سطح و فناوریهای نوین، موسسه پژوهشی علوم و فناوری رنگ و پوششبهزادشیرکوند هداوندگروه پژوهشی رزین و افزودنی ها، موسسه پژوهشی علوم و فناوری رنگ و پوششJournal Article19700101In this study, radiation curable carboxylated urethane acrylate as an anionic polymeric dispersant with dimethylol propionic acid (DMPA), isophorone diisocyanate (IPDI), hydroxyethyl methacrylate (HEMA) in presence of dibutyltin dilaurate (DBTDL) as catalyst and acetone were synthesized. Then the carboxylic groups in dispersants were neutralized with triethylamine (TEA). Molecular structure of anionic polyurethane acrylate dispersants (AUAD) were characterized by fourier transforms infrared spectroscopy (FT-IR). Moreover, the dispersants were used for dispersing of TiO2 and SiO2 and the quality and quantity of particles dispersion were examined by Grindometer. Results show that in presence of carboxylate groups in backbone of polymer significantly reduce the time of dispersing. Also dispersion stability of the particles in the suspension was increased. Also the relationship between the increasing of polyurethane molecular weight and its work as a dispersant was discussed.در این تحقیق، یورتان آکریلات کربوکسیله تابشپز به وسیله دیمتیلول پروپیونیک اسید (DMPA)، ایزوفورن دیایزوسیانات ((IPDI، هیدروکسیاتیل متاکریلات (HEMA) در مجاورت کاتالیزور دیبوتیلتین دیلورات(DBTDL) و حلال استن سنتز شد. سپس گروههای کربوکسیلیک در پراکنشگر یورتان آکریلات تابشپز به وسیله تریاتیل آمین (TEA) خنثی شد. ساختار مولکولی پراکنشگر آنیونییورتان آکریلات به وسیله طیفسنجی تبدیل فوریه زیر قرمز (FT-IR) مشخص شد. علاوه براین، از این پراکنشگرها برای پراکنش ذرات TiO2 و SiO2 استفاده شد و کیفیت و میزان پراکنش ذرات توسط گریندومتر بررسی شد. نتایج نشان دادند به دلیل وجود گروههای کربوکسیلات در زنجیرههای پلیمری میتوان به طور قابل توجهی زمان پراکنش را کاهش و پایداری ذرات در سوسپانسیون را افزایش داد. همچنین رابطه میان افزایش وزن مولکولی یورتان آکریلات کربوکسیله و عملکرد آن به عنوان پراکنشگر مورد بحث قرار گرفت.پژوهشگاه رنگ با همکاری انجمن علمی رنگ ایرانعلوم و فناوری رنگ1735-87798320140923Studying the Anticorrosion, Morphological and Adhesion Properties of an Ambient Temperature Cobalt Induced-Phosphate Coatingمطالعه خواص ضدخوردگی، ریختشناسی و چسبندگی پوشش فسفاته دمای محیط حاوی افزودنی کبالت22122876131FAالهاممتین محمدیدانشکده مهندسی پلیمر و رنگ، دانشگاه صنعتی امیرکبیرمحمدرضامحمدزاده عطاردانشکده مهندسی پلیمر و رنگ، دانشگاه صنعتی امیرکبیربهرامرمضانزادهگروه پوششهای سطوح و خوردگی، موسسه پژوهشی علوم و فناوری رنگ و پوششJournal Article19700101Different properties of an ambient temperature phosphate coating containing cobalt ions were studied on a steel substrate. Surface treatment on the phosphate coating bath was conducted at T=25 ºC, pH=3.1 and t=30 min. Different analytical techniques including linear polarization, scanning electron microscope (SEM), EDX and Pull off test were employed in order to evaluate the phosphate coating properties. The results obtained from the polarization test revealed that corrosion resistance of the phosphate coating was enhanced in the presence of cobalt ions. SEM micrographs showed a better surface coverage for the cobalt induced phosphate coating. Results obtained from the pull off test also showed that the surface treatment of the steel substrate by phosphate coating reduced adhesion loss of the epoxy coating after 30 days immersion in 3.5 wt% NaCl solution. The decrease in the adhesion loss was more pronounced in the case of using cobalt ions in phosphate coating.در این مطالعه، تاثیر افزودنی کبالت بر خواص مختلف پوشش فسفاته تشکیل شده در دمای محیط روی زیرآیند فولادی مورد مطالعه قرار گرفت. پوشش در دمای محیط، 3.1 pH= و زمان30 دقیقه تشکیل شد. از آزمونهای الکتروشیمیایی پلاریزاسیون، میکروسکوپ الکترونی (SEM)،EDX و چسبندگی ((Pull off جهت ارزیابی خواص مختلف پوشش فسفاته استفاده شد. نتایج آزمون الکتروشیمیایی نشان داد که پوشش فسفاته دمای محیط در حضور افزودنی کبالت میتواند خواص ضدخوردگی پوشش فسفاته را بهبود داده و نرخ خوردگی فولاد را بیشتر از پوشش فسفاته فاقد این افزودنی کاهش دهد. تصاویر میکروسکوپ الکترونی بیانگر پوششدهی مناسبتر پوشش فسفاته تشکیل شده در حضور افزودنی نسبت به پوشش فاقد این افزودنی بود. نتایج آزمون چسبندگی pull offافت چسبندگی پوشش اپوکسی در پوشش حاوی افزودنی کبالت به کمتر از نصف میزان پوشش فاقد این افزودنی پس از 30 روز غوطهوری نمونهها در محیط خورنده را نشان داد.پژوهشگاه رنگ با همکاری انجمن علمی رنگ ایرانعلوم و فناوری رنگ1735-87798320140923The Reference Electrode Impedance Effect on the Impedance of the Working Electrode in Corrosion Inhibition Studiesاثر امپدانس الکترود مرجع بر امپدانس الکترود کار در مطالعات بازدارندگی خوردگی22923576132FAمحمدمهدویان احدیگروه پژوهشی پوششهای سطح و خوردگی، موسسه پژوهشی علوم و فناوری رنگ و پوشش0000-0001-8470-6833Journal Article19700101This work intends to study the possible effect of reference electrode impedance on the working electrode impedance. For this purpose, various electrode/electrolyte systems were examined by electrochemical impedance spectroscopy (EIS) using reference electrodes having different impedance. In the experiments, working electrode impedance were around 1 and 10 kohm.cm2; and the reference electrode impedance were in the range of 1-10 kohm. The results showed that utilizing reference electrode with highest impedance resulted in distortion from actual impedance spectra in high or low frequency region which is of particular importance for corrosion inhibition studies.در این تحقیق اثر احتمالی امپدانس الکترود مرجع بر امپدانس الکترود کار مورد بررسی قرار گرفته است. بدین منظور سامانههای مختلف الکترود/الکترولیت با امپدانسهای مختلف همراه با الکترودهای مرجع با امپدانس مختلف مورد آزمایش اسپکتروسکوپی امپداتس الکتروشیمیایی (EIS) قرار گرفت. در آزمایشات، محدوده امپدانس الکترودهای کار 1 و 10کیلو اهم – سانتیمتر مربع و محدوده امپدانس الکترودهای مرجع در محدوده 1 تا 10 کیلو اهم بوده است. نتایج نشان داد، الکترود مرجع با بیشترین امپدانس در برخی از الکترودهای کار میتواند منجر به انحراف از طیف امپدانس واقعی در محدوده فرکانسی بالا یا پایین گردد که این موضوع در مطالعات بازدارندگی خوردگی بسیار حائز اهمیت است.پژوهشگاه رنگ با همکاری انجمن علمی رنگ ایرانعلوم و فناوری رنگ1735-87798320140923Patination of Wood with Diethanolamine: Characteristics and its Resistance Against Weatheringپتینهکردن چوب با دیاتانلآمین: ویژگیها و مقاومت آن در برابر هوازدگی23724876133FAمحسنمحمدیدانشکده مرمت، دانشگاه هنر اصفهانحسیناحمدیگروه مرمت اشیاء تاریخی و فرهنگی، دانشکده مرمت، دانشگاه هنر اصفهانکامبیزپورطهماسبیگروه علوم چوب و کاغذ ، دانشگاه تهرانJournal Article19700101Patination or producing the appearance of age has a great importance in the restoration of historical relics and furniture industry. In this research, patination of white poplar wood (Populus alba L) with Diethanolamine (DEA) and its resistance against weathering was investigated. Treated and untreated samples artificially were weathered for 300 and 800 hours, regarding ASTM 2565-99. Structural changes were investigated by application of Colorimetery, ATR-FTIR spectroscopy and Scanning Electron Microscopy. Results showed that DEA reacts with carbonyl group in hemicelluloses and syringyl unit of lignin. It causes to increase of darkness, yellowness and redness of wood. In the first stage of weathering (300 hours) photo-oxidation of lignin localized on guaiacyl unit, but in the second stage (800 hours) syringyl unit of lignin was degraded. Patination does not protect the white poplar wood against weathering for long time.ایجاد ظاهر قدیمی در سطح چوب یا پاتین، اهمیت زیادی در فرآیندهای مرمت آثار تاریخی و همچنین ساخت مبلمان دارد. در این پژوهش چوب کبوده (Populus alba L) پتینهشده با استفاده از تیمار دی اتانل آمین و مقاومت آن در برابر هوازدگی مورد مطالعه قرار گرفت. هوازدگی مصنوعی براساس دستورالعمل ASTM 2565-99 در دو مرحله 300 و 800 ساعت انجام شد. ارزیابیها با استفاده از رنگسنجی، طیفسنجی زیر قرمز- بازتاب کل تضعیف شده تبدیل فوریه و میکروسکوپ الکترونی روبشی انجام شد. نتایج نشان داد که دیاتانلآمین بیشتر با گروه کربونیل در همیسلولز و واحد سرینجیل در لیگنین واکنش میدهد و باعث افزایش تیرگی، قرمزی و زردی چوب میگردد. در مرحله اول هوازدگی (300 ساعت) فتواکسیداسیون لیگنین در واحد گواییاسیل متمرکز گردید ولی در مرحله دوم (800 ساعت) واحد سرینجیل نیز دچار تخریب شد. پتینهکردن چوب کبوده در طولانی مدت از تخریب ناشی از هوازدگی جلوگیری نمیکند.پژوهشگاه رنگ با همکاری انجمن علمی رنگ ایرانعلوم و فناوری رنگ1735-87798320140923A Concise Review on Color Match Prediction Modelsمروری اجمالی بر مدلهای پیشگویی رنگ24926076134FAمهزیارگرجی بندپیگروه پژوهشی نمایش رنگ و پردازش تصویر، موسسه پژوهشی علوم و فناوری رنگ و پوششکیوانانصاریگروه پژوهشی نمایش رنگ و پردازش تصویر، موسسه پژوهشی علوم و فناوری رنگ و پوششفرهادعامریگروه پژوهشی فیزیک رنگ، مؤسسه پژوهشی علوم و فناوری رنگ و پوششسیامکمرادیانقطب علمی رنگ، موسسه پژوهشی علوم و فناوری رنگ و پوششJournal Article19700101In order for a color matching model to be able to predict the correct and precise amounts of colorants to achieve a certain color, numerous sets of information regarding the effective parameters of the colored system is required. These parameters include the absorbance and scattering coefficients of colorants, relations between total and internal reflection of a colored layer, basic assumptions relating to incident light interactions with and without the colored layer, geometry and size of the scattering particles, etc. Additionally a colored layer could be transparent, translucent or opaque. Various models such as physical, numerical, intelligent and hybrid models attempt to present a correct prediction of the amounts of components to give the precise color through determining the contribution of each effective parameter which may lead to new formulae. In the present study, a variety of such models and their various applications are reviewed. Most of the well-known physical models such as Kubelka-Munk, Four-Flux, Many-Flux, Chandrasekhar, inverse adding doubling, Monte Carlo, representative layer theory and even intelligent models such as artificial neural network models for optimal usage are herewith described.برای آن که یک مدل رنگ همانندی بتواند پیشگویی صحیح و دقیقی از مقادیر مواد رنگی اولیه مورد نیاز ارائه دهد، نیاز به شناخت عوامل موثر و لحاظ شرایط سیستم رنگ در آن است. از جمله این عوامل، تعیین ضرایب جذب و انتشار مواد رنگی، ارتباط میان انعکاس کلی و انعکاس داخلی لایه رنگ، فرضهای اولیه در خصوص نور تابیده به لایه رنگ، هندسه انتشار و اندازه ذرات و سایر موارد میباشد. همچنین یک لایه رنگ، ممکن است شفاف، نیمهشفاف و یا پشتپوش باشد. مدلهای مختلف همچون مدلهای فیزیکی، مدلهای عددی و مدلهای هوشمند و هیبریدی با تعیین عوامل موثر و ارائه فرمولهای جدید، سعی در مدلسازی و در نتیجه ارائه یک پیشگویی صحیح از رنگ نهایی در شرایط خاص تعریف شده دارند. در این مطالعه سعی در بررسی این مدلها و شرایط استفاده از آنها در کاربردهای مختلف شده است. برخی از شناختهشدهترین این مدلها مانند کیوبلکا- مانک، تئوری چهار پرتویی، تئوری چند پرتویی، چاندراسخار، افزایشگر دوتایی معکوس، مونت کارلو، لایه نماینده و امکان استفاده از روشهای هوشمند مانند شبکه عصبی نیز که به نظر میرسد نتایج خوبی را ارائه میدهند، مورد بررسی اجمالی قرار گرفته و شرایط اولیه لازم برای استفاده بهینه از آنها بیان شده است.